Did some research, seems like it's better to use an Al uicp. The prob is that alky is corrosive to Al, and is not to SS. What do you guys think? an alternative would be to run a SS uicp and wrap it with an insulator.

Plz let me have your opinions,


Tks

 

you wont be injecting enough meth to significantly corrode your uicp, plus when meth is injected it is vaporized/dried almost immediately. the biggest concern will be ensuring that your meth nozzle does not drip or leak when its not on or injecting.

remember that the IM/Head is aluminum

 

I would go with aluminum just for the weight savings. as noted above the Im/HEAD is al. as is the fuel rail&t/b.